Zinc aluminium spray

Container: 400 ml spray can

Technical data: Colour: RAL 9006, similar to if surface was hot-dip galvanised Areas of application: indoors and outdoors Binder: acrylic resin Pigments: zinc and aluminium pigments Pigment purity: approx. 99.5% Al / approx. 94% Zn Metal content in the dry film: approx. 51% Specific weight: 0.90 - 1.0 g/cm³ Recommended primer: zinc spray Processing temperature: from +5°C to +35°C (optimum +18°C to +35°C) Consumption with 1.5 cross-coat approx. 150 ml/m² Layer thickness with 1.5 cross-coat approx. 20-40 μm Dust dry after approx. 15 min. Fully hardened after approx. 12 h Can be painted after approx. 12 h Abrasion-resistant Cross cut DIN 53151 / ISO 2409 Cross cut value GT 0 to GT 1 Salt spray test ISO 9227 > 450 h Mandrel flex test DIN EN ISO 1519 no hairline crack formation Top coat not required Temperature resistance after complete hardening approx. -50°C to +300°C Storage stability 24 months